简介：BondingofAl2O3tocuisperformeddirectlyusingTifoilattemperatureof1273K.Themicrostructureofthejointinterfaceisinuestigatedthroughscanningelectronmicroscope（SEM）,electron.probemicroanalysis（EPMA）andX-raydiffraction（XRD）.theeffectoftheinitialtifoilthicknessonthereactionlayerthicknessandthejointStrengthareinvestigated.

简介：

简介：Dynamicsinpartialtransientliquidphasebonding(PTLPbonding)ofSi3N4ceramicwithTi/Cu/Timulti-interlayerwassystematicallystudiedthroughmicro-analysisofjointinterfaces.Theresultsshowthatgrowthofreactionlayerandisothermalsolidificationprocessiondoatthesametime.GrowthofreactionlayerandmovingofisothermalsolidificationinterfaceobeytheparaboliclawgovernedbythediffusionofparticipatingelementsduringthePTLPbonding.Coordinationoftheabovetwodynamicsprocessisdonethroughtimeandtemperature.Whenreactionlayerthicknessissuitableandisothermalsolidificationprocessisfinished,thehighbondingstrengthatroomtemperatureandhightemperatureareobtained.

简介：ThispaperintroducesabrazingprocessbetweenAl_2O_3ceramicandInvaralloy.Al_2O_3canbebrazedwithInvareffectively.TheinterfacialstructureofAl_2O_3/Invarjointcanbeexpressedas:Invar/Ag(s,s)+Cu(s,s)+Fe_2Ti(zoneⅠ)/Ag(s,s)+Cu(s,s)+Fe_2Ti+NiTi+Cu_3Ti(zoneⅡ)/Ag(s,s)+Cu(s,s)+Cu_2Ti+Al(s,s)+TiC+TiO(zoneⅢ)/Al_2O_3.Themaximumshearstrengthof139MPawasmeasuredforas-brazedAl_2O_3/Invarjointbrazedat850℃for25minor900℃for15min.

简介：本文针对N4／1Cr18Ni9Ti与N4／0Cr25Ni20复合板的特殊焊接要求，根据NB／T47014—2011《承压设备焊接工艺评定》的要求，制备2块N4／1Cr18Ni9Ti试板，2块N4I／0Cr25Ni20试板，尺寸均为500mmX150mmX（4＋14）mm。不锈钢基层采用GTAW打底，焊丝选用HOCr21Ni10，SMAW填充与盖面，焊条选用A302与A402。镍复层的焊接采用手工钨极氩弧焊，焊丝选用含Ti、AI等脱氧元素的ERNi-1焊丝，保护气体选择98％Ar＋2％H2。试板焊接完成，外观检验合格后进行100％RT，检测结果符合JB厂r4730，2—2005I级合格，镍复层进行100％PT，检测结果符合JB／T4730．5—2005I级。两种焊接试板分别取样并做拉伸、弯曲力学性能分析，镍复层焊缝做化学成分分析。通过两块焊接试板试验对比，不锈钢基层焊接材料选择HOCr21Ni10焊丝与A302焊条。镍复层焊接采用ERNi-1焊丝，焊接保护气体为98％Ar＋2％H2。通过焊接工艺评定试验研究，解决了N4／1Cr18Ni9Ti与N4I／0Cr25Ni20复合板焊接问题，提高了用户坩埚的返修质量与再次使用寿命，为使用单位节约了成本。

简介：ThedistributionsoftheaxialstressandshearstressinAl2O3-TiC/Q235diffusionbondedjointswerestudiedusingfiniteelementmethod(FEM).Theeffectofinterlayerthicknessontheaxialstressandshearstresswasalsoinvestigated.Theresultsindicatethatthegradientsoftheaxialstressandshearstressaregreatnearthejointedge.ThemaximalshearstressproducesattheinterfaceoftheAl2O3-TiCandTiinterlayer.WiththeincreaseofCuinterlayerthickness,themagnitudesoftheaxialstressandshearstressfirstdecreaseandthenincrease.Thedistributionoftheaxialstresschangesgreatlywithalittlechangeintheshearstress.TheshearfractureinitiatesattheinterfaceoftheAl2O3-TiC/TiinterlayerwithhighshearstressandthenpropagatestotheAl2O3-TiCside,whichisconsistentwiththestressFEMcalculatingresults.

简介：

简介：

简介：Thenormallycenteredelectronbeamandnon-centeredelectronbeamweldingofTiAltoTC4wasinvestigatedinordertoanalyzetheelectronbeamweldabilitybetweenTiAl/TC4dissimilarmaterials.MacroscopiccoldcrackeasilyoccurrednearTiAlsubstrateinthejoints.Theoptimaltensilestrengthwasrelatedtotheweldingheatinput.Theweldstructureswerecomposedofbulkycolumnargrainsandequiaxedgrains.Theisolatedphasesconsistedoflargequantitiesofα2-Ti3Alphase,smallquantityofB2phase,γ-TiAlphaseandYAl2phase.InsufficientmeltingofthebasemetaloccurredintheweldwhenthebeampositionleanedtotheTC4side.Thetensilestrengthcouldbeimprovedwhenthedeflectionwaslimitedintheoptimumrange.Otherwise,non-fusionzonewaseasilygeneratedintheweld,whichledtothelowtensilestrength.

简介：ＴｈｅｒｍａｌｂｅｈａｖｉｏｒｏｆＢ４Ｃｐａｒｔｉｃｌｅｓｕｎｄｅｒｐｌａｓｍａａｒｃｐｏｗｄｅｒｓｕｒｆａｃｉｎｇｃｏｎｄｉｔｉｏｎ￥ＷＡＮＧＸｉｂａｏ；ＺＨＡＮＧＷｅｎｙｕｅ；ＬＵＴｏｎｇｌｉａｎｄＰＥＮＧＪｉｅ(ＨｅｂｅｉＵｎｉｖｅｒｓｉｔｙ...

简介：

简介：

简介：本文介绍了低温(-50℃)乙烯球罐制造和焊接技术,制定了球罐制造工艺流程和球壳板成形工艺,通过试验确定了焊接预热温度、层间温度和后热温度,并正确选择了焊接材料。制定了乙烯球罐的焊接工艺规范,并成功地完成了低温(-50℃)乙烯球罐的制造和焊接。

简介：

简介：Anewhardfacingprocess,reactivebrazecoatingprocess(RBCC)wasstudied,and(TiC+Cr3C2)/FecompositecoatingswerepreparedbyRBCCusingcarbon,Cr3C2,iron,ferrochromiumandtitaniumpowderastherawmaterialsinvacuumbrazefurnace.TheresultsshowthatTiCisin-situsynthesizedinthecoatings.ThemethodsofintroducingCr3C2havegreateffectsonthedistributionofTiC.AddingCr3C2directlytotherawmaterialsforcoatings,fineTiCparticlesaggregateintodiscoidsparalleltothecoatingsurface,whereas,in-situsynthesizingCr3C2incoatings,theaggregationsofTiCarelumpish.Duringbrazecoating,Cr3C2particlesdirectlyaddeddissolveandprecipitatetobecomeneedle-shaped.Thecoatingshaveanevenandsmoothsurfaceandarecombinedwiththeirmildsteelsubstratesbyametallurgicalbonding.

简介：1999年由TWI代表国际搅拌摩擦焊专利协会，在美国加利福尼亚成功举办第一届搅拌摩擦焊国际会议，此后，每两年一届分别在不同国家成功举办了九届搅拌摩擦焊国际会议。

简介：TheHAZmicrostructureandperformanceofQuenchingandTemperingmodetemperbeadweldingandgeneralweldedjointswhichweremadeonSA508-3steelof60mmthicknesswerecomparedinthisarticle.Theresultshowsthattemperingsorbitewhichhasexcellentoverallperformancewasobtainedinbothmodes.ThemicrostructureofQuenchingandTemperingmodeweldedjointsgotmorefinegrain.Eventhoughthehardnessoftemperingbeadweldedjointsishigherthanthegeneralone,itstillmeetsthestandardswhichislowerthan350HV.TheimpactabsorbingenergyofeachdistrictoftemperingbeadweldedjointsHAZreached170J,whichisequaltogeneralone.

简介：

简介：Fe3AlandCr18-Ni8steelwerebondedinvacuumandaninterfacewasformedbetweenFe3AlandCr18-Ni8steel.Stressdistributionatthediffusion-bondedinterfacewasresearchedbynumericalsimulationandfiniteelementmethod(FEM).TheresultsindicatedthatthepeakstressappearedattheinterfacenearCr18-Ni8steelside.Thisisthekeyfactortoinducecrackatthisposition.Withtheenhancementofheatingtemperature,thepeakstressatthebondedinterfaceincreases.Whenthetemperatureis1100℃,thepeakstressisupto65.9MPa,whichisbiggerthanthatat1000℃by9.4%.Inaddition,thepeakstressbecomesbiggerwiththeincreaseofthethicknessofbasemetalfrom1mmto8mm.Whilethethicknessismorethan8mm,thepeakstressvariesslightlywiththechangeofthethickness.

简介：