简介：

简介：SY508-3-166[篇名]Effectsofboronadditiononheatingprocessesofmartensitein0.1C-9Cr-3W-Costeels;SY508-3-167[篇名]Developmentofamulti-attributeselectionprocedurefornon-traditionalmachningprocesses，……

简介：[篇名]ClosedloopinteractionofgeneticalgorithmsandparalleltemperinginthehybridGAPToptimizationalgorithm，[篇名]Inductionhardeningandtemperingofcriticalpowertraincomponents:aSHarP-Capproachtoreversingthetrendofpriceforquality，[篇名]LifeimprovementofTiN-duplex-treatedtoolsteelbytempering，[篇名]Experimentalstudiesofusingwatermistcoolingforthetemperingofglass，[篇名]High-speedhigh-precisiontemperingandstressrelieving。

简介：

简介：

简介：TheinfluenceofnitrogenonthestructureandpropertiesofFe-10Cr-NandFe-10Cr-IMo-Nsteelsaftertemperinginthetemperaturerangeof650-750℃.In-situheattreatmentsystemusingYAGlasersourcetemperingprocessafterquenching.ModellingandcharacterizationofMo{sub}2CprecipitationandcementitedissolutionduringtemperingofFe-C-Momartensiticsteel.Inductiveheatingforhardeningandtemperingofsteelrails.Rapidtemperingandstressreliefviahigh-speedconvectionheating.

简介：本文简要介绍乌克兰，俄罗斯等国家生产的一种脆性金刚石的品种，粒度，特性，生产过程及用途，供同行参考，以便受到启发，开辟一条创造经济效益的新途径。

简介：叙述了模具钢经真空回火后的着色现象以及真空回火的必要性。

简介：钛合金螺钉在装配过程中发生断裂失效，对装配和模拟扭转试验过程中断裂的钛合金螺钉断口进行了宏微观观察和能谱成分分析，对同批次螺钉进行了应力持久试验，对失效钛合金螺钉的金相组织进行了检查。结果表明，螺钉的断裂性质相同，均为脆性断裂；螺钉断裂的主要原因是存在内部缺陷，而与氢致脆性断裂的关系不大；螺钉的内部缺陷可能是在锻造过程后期由于某种偶然因素造成了原始β晶界开裂所致。

简介：通过断口观察、化学成分分析、金相组织检查、硬度检测、拉伸及冲击试验等方法，对某大型锻造法兰脆性断裂原因进行了分析。结果表明：粗大的魏氏体组织是造成法兰发生脆性断裂的直接原因，阐述了粗大组织对法兰脆性断裂的影响机制；证明了这种组织缺陷与热处理时工件过热有关，可通过正确的正火工艺来消除，并且采用了正确的热处理工艺，材料的冲击功提高了2个数量级，解决了锻造法兰的脆性问题。

简介：针对20Mn2结构钢圆环链拉伸试验时出现脆性断口的现象，经断口宏微观观察、金相分析后，认为圆环链的断裂性质为沿晶脆性断裂。分析认为，出现沿晶脆断是由于回火温度过高，且圆环链加工现场受场地限制，热处理后的成品链堆放在一起，造成内部圆环链冷却速率较慢，致使Si、Mn、P等元素在奥氏体晶界偏聚富集，形成高温回火脆性。利用合金结构钢高温回火脆性的可逆性，该批圆环链经670℃保温1h重新回火后，用油快速冷却，消除了高温回火脆性，经检验完全合格。

简介：采用能量守恒定律,推导出岩石热-水-力(THM)耦合条件下含裂纹试件的裂纹扩展起裂速度的计算公式。利用自行设计的THM耦合断裂导电胶电法,实时连续地测量出裂纹扩展速度。研究结果表明:起裂速度随着温度和水压的增加而增加。计算结果与试验结果吻合较好,从而验证了所推导的THM耦合断裂起裂速度计算公式的正确性。