Silvernanowires（AgNWs）withdiameterof90--150nmandlengthof20--50μmweresuccessfullysynthesizedbyapolyolprocess.Grapheneoxide（GO）waspreparedbyHummersmethod,andwasreducedwithstronghydrazinehy-drateatroomtemperature.Theflexibletransparentconductivefilms（TCFs）werefabricatedusingthemixedcelluloseeater（MCE）asmatrixandAgNWsandreducedgrapheneoxide（rGO）asconductivefillersbytheimprovedvacuumfiltrationprocess.Then,theoptical,electricalandmechanicalpropertiesoftheAgNWs-rGOfilmswereinvestigated.TheresultsshowthatfortheAgNWs-rGOfilmproducedwiththedepositiondensitiesofAgNWsandrGOas110mg.m2and55mg·m^-2,theopticaltransmissionat550nmis88.4%withRsaround891Ω·sql,whereastheopti-caltransmissionfortheAgNWs-rGOfilmwithdepositiondensitiesofAgNWsandrGOof385mg·m^-2and55mg·m^-2is79.0%at550nmwithRsaround9.6Ω·sql.ThereislittleovertincreaseinRsoftheAgNWS-rGOfilmaftertapetestsfor200times.ThebendingtestresultsindicatethatthechangeinRsofAgNWs-MCEfilmislessthan2%evenafter200cyclesofcompressiveortensilebending.TheexcellentmechanicalpropertiesoftheAgNWs-rGOfilmcanbeattributedtotheburyingofAgNWsandrGOatthesurfaceofMCE.