简介:ThemorphologyandcorrosionbehaviorofNi/Al2O3compositecoatingspreparedusingdouble-pulsedelectrodepositingtechniqueafteroxidizedunder800℃NaCldepositinairenvironmentwereanalyzedbyscanningelectricalmicroscope(SEM),X-raydiffraction(XRD)andenergydispersivespectrum(EDS).TheresultsshowedthatthecorrosionofallcompositecoatingswasacceleratedunderNaCldeposits,andthecorrosionproductswereratherporouswithpooradherencetothematrix.Al2O3particlesinthecoatingscanrefinethegrainsizeandimprovethehightemperaturecorrosionresistanceofthecoatings.Withinthetestscope,themoreAl2O3particlesinthecoatings,thelowercorrosionratescouldbeobtained,andthecorrosionmechanismwasalsodiscussed.
简介:TheelectrodeprocessofY3+iononmolybdenumandnickelelectrodeshasbeenstudiedbycyclicvoltammetryandchronopotentiometryintheYCl3-NaCl-KClmelt.Theoverallchargetransferprocessisatwo-stepreaction:Y3++e=Y2+;Y2++2e=Y.YttriumreducedonthenickelelectrodecanformaseriesofNi-Yalloys.X-raydiffractionanalysiswasemployedtodeterminethealloycompositionsformedunderdifferentcon-ditions.