简介：目前，904L锻材、904L热轧卷板在太钢相继试制成功，这是太钢继成功开发出国内第一块904L中厚板以来超级奥氏体不锈钢“家族”再添的新成员。标志着太钢在拓宽不锈钢高端产品领域、在国家高、精、尖不锈钢品种的研究水平又有了新的突破。

简介：309Lisakindofausteniticstainlesssteel.Thispaperdiscusses309L,whichwassmeltedandrolledinalab.Itsmicrostructuralcharacteristicsinstatesofas-cast,hot-rolling,cold-rollingandsolidsolutionwereinvestigatedrespectivelybyopticalmicroscope(OM).Itisfoundthat309Liscomposedofausteniteandresidualδ-ferriteundertheseconditions,andtheδ-ferritecannotbeeliminatedeasilybyheat-treatment.Itshotplasticityanddeformationresistancewereinvestigatedinaseriesofheatsim...

简介：Twothermo-mechanicalcontrolledprocesses(TMCP)includingcontrolledrollingandacceleratedcoolingareproposedfortheproductionofheavygaugeSUS304Lausteniticstainlesssteelplateswithdifferentstrengthsandothercharacteristics.BasedontherecrystallizationmechanismandcarbideprecipitationbehaviorofSUS304Lausteniticstainlesssteel,TMCPprovidesapowerfulmeanstocontrolthemicrostructureandprecipitationofthehotrolledsteelplatebythecontrolledrollingandacceleratedcoolingprocess.Thedislocationdensityandgrainsizearethemainfactorsindeterminingthestrengthofthestainlesssteelplates.Therefore,itisnecessarytostrictlycontrolthehotrollingparameters,includingparameterssuchasthefinishhotrollingtemperatureintherecrystallizationtemperatureregionandthetotalreductioninthenon-recrystallizationregion.Furthermore,inordertoavoidcarbideprecipitationandguaranteetheintergranularcorrosionresistanceofTMCPSUS304Lausteniticstainlesssteel,acriticalcoolingrateafterrollingisdetermined.

简介：316Lstainlesssteelcoatingswerepreparedbycoldgasdynamicspraying(CGDS)onacarbonsteel.Anewheaterofsprayedpowderswasaddedtothetraditionalfacility.Theresultsshowthatthecoatingqualityisobviouslyimproved,duetobetterinterfacebondingandreducedporosity.

简介：焦化厂的硫酸铵饱和器,常常由于检修焊接不当加之强腐蚀工艺介质剧烈腐蚀之下,造成焊接接头的腐蚀破坏,形成晶间腐蚀、裂纹、穿孔等焊接接头缺陷和危害。因而,本文从316L不锈钢的焊接性入手,分析其晶间腐蚀,焊接热裂纹,应力腐蚀开裂,接头的σ相脆化等该材质的焊接特点,并详述了其防止的具体措施。结合实际有针对性的阐述了其该母材的焊接工艺及要点,有效的降低316L不锈钢的晶间腐蚀及其他焊接缺陷,提高了其焊接性。

简介：通过409L不锈钢板材表面线鳞缺陷检验、工艺状态及TiN形成热力学分析，认为导致409L板材表面线鳞缺陷原因主要是钛的夹杂物。钛的夹杂物来源于炼钢生产过程大量TiN的析出。解决这一问题的关键在于控制钢中的氮含量，在现有工艺装备条件下，重点是减少炼钢过程的增氮量。根据这一思路，制定相应措施，有效抑制了线鳞缺陷的批量发生。

简介：韩国浦项钢铁公司下属的设备专业制造企业POSCOPlantec于2014年12月29日称，全球首次采用904L超级奥氏体不锈钢中厚板制造出用于生产液化石油气的罐体，并已向三星重工发货。

简介：FSWandTIGwereconductedon316Lstainlesssteel.Variationduringmicrostructureandpropertiesinjointsobtainedbydifferentweldingmethodswasstudied.TheresultsshowthattheeffectofseveremechanicalstirringandintenseplasticdeformationcreatafinerecrystallizedgrainintheweldingjointduringFSW.AsforTIG,thetemperatureofweldingjointexceedsthemeltingpointofweldedmaterialitself.Theentireweldingprocessbelongstothesolidificationofasmallmoltenpool;andthemicrostructureofthejointtakesonatypicalcastingstructure.Whentheweldingparameterswereselectedappropriately,theaverageultimatetensilestrengthofFSWjointscanreach493MPa,whichis83.6%ofbasemetal;theaverageelongationis52.1%ofbasemetal.TheaverageultimatetensilestrengthofTIGjointsis475MPa,whichis80.5%ofbasemetal;theaverageelongationis40.8%ofbasemetal.ThetensiletestofFSWjointsissuperiortotheTIGjoints.ThemicrohardnessofFSWjointcomparedtobasemetalandTIGjointhavingasignificantimprovement,whicharel95.5HV,159.7HVand160.7HV,respectively;grainrefinementstrengtheningplaysanimportantroleinenhancingthemicrohardness.TheelectrochemicalcorrosiontestsshowthatthejointofFSW316Lausteniticstainlesssteelhasagoodcorrosionresistance.

简介：采用100tUHP电炉短流程生产L245NCS，通过实施精料方针、规范脱氧工艺、优化吹氩处理工艺、选择最佳二冷区配水模型、采取钢水低过热度浇注浇注、控制拉速、控制轧制温度等，产品能够满足市场需求。

简介：TheFe-Ti-Nmateralloywaspreparedthroughthein-situreactionofnitrogengaswiththeFe-Timelt.ScanningelectronmicroscoperesultsshowthattheparticlesuniformlydistributedintheironmatrixwereTiN.ThedeliberatelypreparedFe-Ti-Nmasteralloywasemployedforthe409Lferriticstainlesssteelinanattempttorefinetheas-castsolidificationstructure.ItwasfoundthattheeffectivenessofFe-Ti-Nmasteralloyonrefiningoftheas-cast409Lferriticstainlesssteelwasaffectedbyadditionlevel,holdingtimeandmeltstemperature.Itwasfoundthattheaverageequiaxedgrainsizedecreasedfrom1503μmto303μm,theproportionofequiaxedgrainzoneincreasedfrom14%to100%withincreasingtheFe-Ti-Nmasteralloyadditionlevelto2.5%.Theproportionofequiaxedgraindecreasedfrom85%to4%asthesolidificationtemperatureincreasedfrom1803Kto1883K.Whentheholdingtimereachedto8min,thesolidificationstructuresof409Lferriticstainlesssteelshowextremepointsintheproportionofequiaxedgrain.Itisclearthatthegrainrefiningefficiencygraduallyfadeawaywiththeincreasingoftheholdingtimeattheverybeginning.However,whentheholdingtimecontinuestoincreaseandexceedstheextremepoint,thegrainrefiningefficiencyoftheFe-Ti-Nmasteralloyrecoveredtoacertaindegree.Theexperimentalresultsmentionedabovehavebeenanalyzedintermsofthermodynamics.Underappropriateconditions,theFe-Ti-Nmasteralloyusedforgrainrefinementofthesolidificationstructureof409Lferriticstainlesssteelmayhavegoodprospectsforindustrialapplications.

简介：本文通过将SUS304、SUH409L、06Cr13三种不锈钢在35℃,6%FeCl3＋HCl的混合溶液中进行点腐蚀试验,将腐蚀后腐蚀速率、宏观特征、微观组织特征、形貌特征等进行了阐述及对比,并根据化学成分、微观组织结构、腐蚀后的形貌特征等进行了腐蚀原因分析。