简介：从表面纵裂形貌、结晶器冷却、过热度与拉速、专用保护渣、弱冷工艺等方面分析27SiMn圆坯表面纵裂成因,并从专用保护渣、拉速和过热度匹配、结晶器液面波动以及二冷配水等方面提出改善措施,以保证圆坯表面质量。

简介：Inthisstudy,metallographicanalysisandnanoindentationcharacterizationwereusedtoanalyzethepropertiesandmicrostructuresofas-castnitrogenalloyed27Cr-7Ni-4Mosuperduplexstainlesssteel(super-DSS).Theas-castmicrostructureofthesuper-DSSwascharacterizedbyitsferriteandisland-likeaustenitephases.Duringthesolutionannealingprocess,theaustenitevolumepercentageofthesteeldecreasedgraduallywithincreasedannealingtemperature.Asamainelement,thechromiumcontentintheferriticandausteniticphaseselevatedslightlyatfirstthendecreasedwithincreasedannealingtemperature.Thechromiumpartitioncoefficientinthesteelvariedbyaround1.0.Thecontentsofnickel,anothermainalloyelement,alsoincreasedintheferriticandausteniticphaseswithincreasedannealingtemperature,asdidthenickelpartitioncoefficientinthesteel,whichtendedtobecloseto1.0.Thenanoindentationcharacterizationresultsindicatethatthehardnessoftheaustenitephaseisslightlygreaterthanthatoftheferritephase.Theyweresimilartoeachotherwithinacertaintemperaturerangefrom1050℃to1100℃.Thistemperaturerangewasconsistentwiththetemperaturerangeinwhichthecontentratioofthetwophaseswascloseto1∶1.WefoundtheYoung'smodulusoftheferritephasetobegreaterthanthatoftheaustenitephase.Withincreasedannealingtemperature,theYoung'smodulusoftheferritephasedecreasedwhilethatoftheaustenitephaseremainedalmostunchanged.