简介:ThispaperintroducesabrazingprocessbetweenAl_2O_3ceramicandInvaralloy.Al_2O_3canbebrazedwithInvareffectively.TheinterfacialstructureofAl_2O_3/Invarjointcanbeexpressedas:Invar/Ag(s,s)+Cu(s,s)+Fe_2Ti(zoneⅠ)/Ag(s,s)+Cu(s,s)+Fe_2Ti+NiTi+Cu_3Ti(zoneⅡ)/Ag(s,s)+Cu(s,s)+Cu_2Ti+Al(s,s)+TiC+TiO(zoneⅢ)/Al_2O_3.Themaximumshearstrengthof139MPawasmeasuredforas-brazedAl_2O_3/Invarjointbrazedat850℃for25minor900℃for15min.
简介:Theobjectiveofthisstudyistoinvestigatetheinfluenceofaddingtinyamountofmixedrareearth(La,Ce)andSrtoAl-20Cu-5Si-2Nifillermetal,byanalyzingthemicrostructure,wettabilityandmechanicalpropertiesofbrazedjoints.Theresultsshowthawiththeadditionofmixedrareearth(La,Ce)intoAl-20Cu-5Si-2Nialloy,theα-AlsolidsolutionaswellasCuAl_2(Ni)intermetalliccompoundphasesignificantlyreduced,whilemoreAl-SieutecticphaseandAl-Si-Cuternaryeutecticphasewereproduced.Andasmixedrareearth(La,Ce)addedin,thewettabilityofAl-20Cu-5Si-2Nifillermetaldecreased,whiletheshearstrengthofthebrazedjointsincreased.TheadditionofMinorSrmodificatedAl-20Cu-5Si-2Nifillermetal,furtherreducedtheCuAl_2(Ni)intermetalliccompoundphase,whichwaspartiallyreplacedAl-Si-Cuternaryeutecticphase.Asaresult,thetensilestrengthaswellasthewettabilityofthefillermetalwasimproved.
简介:Thispaperintroducedthebasictheoryandalgorithmofthesurrogatedatamethod,whichproposedarigorouswaytodetecttherandomandseeminglystochasticcharacteristicsinasystem.TheGaussiandataandtheRosslerdatawereusedtoshowtheavailabilityandeffectivityofthismethod.Accordingtotheanalysisbythismethodbasedontheshort-circuitingcurrentsignalsundertheconditionsofthesamevoltageanddifferentwirefeedspeeds,itisdemonstratedthattheelectricalsignalstimeseriesexhibitapparentlyrandomnesswhentheweldingparametersdonotmatch.However,theelectricalsignalstimeseriesaredeterministicwhenamatchisfound.Thestabilityofshort-circuitingtransferprocesscouldbejudgedexactlybythemethodofsurrogatedata.