简介:[篇名]ParentphaseageingandmartensitestabilizationinCu-Al-Nibasedmeltspunshapememoryribbons,[篇名]ISSUESRELATEDTODURABILITYOFFRPREINFORCEMENTFORRCSTRUCTURESEXPOSEDTOACCELERATEDAGEING,[篇名]AgeingofelectricalinsulationmaterialsusingaTeslatransformer,[篇名]Impactofageingontribologicalpropertiesofenvironmentallyfriendlyhydraulicfluids,[篇名]Comparisonofdifferentneuralnetworksalgorithmsusedinthediagnosisandthermalageingpredictionoftransformeroil,[篇名]Voltageresponsemeasurementsforpowertransformermoistureandageingconditionassessment,[篇名]Newtechnologyinanageingassetbase,[篇名]Usingequivalentfailureratestoassesstheunavailabilityofanageingsystem
简介:Ageingeffectoncreep-fatiguepropertiesofsuper-clean9%CrMoVsteelforsteamturbinerotorsofcombinedcyclepowerplants.EXPERIENCElNMANAGEMENTOFAGElNGOFBRlDGESINEASTERNEUROPE.Transportpolicyforanageingpopulation.Ageingofimpregnatingliquidswithdifferentchemicalstructureforpolypropylenecapacitordielectric.
简介:对比研究一种新型三级时效制度(T76+T6)和常规回归再时效制度(RRAT77)对7150铝合金型材耐腐蚀性能的影响。选取三种腐蚀溶液(3.5%NaCl;10mmol/LNaCl+0.1mol/LNa2SO4;4mol/LNaCl+0.5mol/LKNO3+0.1mol/LHNO3),分别对7150铝合金型材进行开路电位、循环极化曲线以及电化学阻抗谱的表征。讨论自腐蚀电位、点蚀电位、点蚀转换电位以及电位差值等参数对铝合金腐蚀表征的适用性与局限性。电化学与扫描电镜(SEM)结果表明,相比于传统RRAT77制度,T76+T6时效制度处理的铝合金在没有强度损失的前提下,具备更好的耐点蚀、耐晶间腐蚀以及耐剥落腐蚀的能力。这是由于该新型三级时效制度处理的铝合金的晶界析出相进一步粗化和断续分布所致。
简介:利用X射线衍射分析(XRD)、差示扫描量热法(DSC)和拉伸试验,研究不同温度等通道转角挤压(ECAP)和常规静态时效处理后6013Al-Mg-Si铝合金的微观结构、时效行为、析出动力学以及力学性能。XRD测得的ECAP变形后合金的平均晶粒尺寸在66-112nm范围内,平均位错密度在1.20×10^14-1.70×10^14m^-2范围内。DSC分析表明,由于ECAP后试样比常规时效处理试样拥有更细小的晶粒和更高的位错密度,因此,ECAP变形后合金的析出动力学更快。与未变形合金相比,ECAP后试样的屈服强度和抗拉强度都得到了显著提高。室温ECAP后试样的强度达到最大,其屈服强度是静态峰时效屈服强度的1.6倍。细晶强化、位错强化以及由于ECAP过程中的动态析出而产生的析出相强化,是ECAP合金获得高强度的几种主要强化机制。